Stable, low viscosity polymer/polyisocyanate dispersion made using a macromolecular monomer and a functional monomer

ABSTRACT

A stable, low viscosity polymer/polyisocyanate dispersion wherein the polymer is produced by polymerizing an ethylenically unsaturated macromolecular monomer, a functional monomer, and another ethylenically unsaturated monomer, together with a polyurethane foam, elastomer, adhesive, sealant, or coating produced therefrom and a method for fabricating the foam.

FIELD OF THE INVENTION

The present invention relates generally to polymer/polyisocyanate dispersions and, more specifically, to such dispersions characterized by stability and low viscosity.

BACKGROUND OF THE INVENTION

In the production of polyurethane foams, elastomers, and coatings, a polyol is reacted with a polyisocyanate in the presence of a urethane catalyst. It is well established in the art that physical properties of these foams, elastomers, adhesives, sealants, and coatings can be enhanced by incorporating solids as an organic filler into the polyol side of a polyurethane formulation (i.e., the so-called "B-side") in the form of dispersed polymer particles prior to the urethane-forming reaction. More specifically, it is known that high levels of dispersed polymer are desired since the firmness of the resulting foams and elastomers, generally expressed as load-bearing capacity or modulus, is thereby enhanced. By way of illustration, U.S. Pat. No. 4,454,255 discloses a method of preparing high non-urethane polymer content dispersions in polyols of greater than 30 percent, based on the total polymer plus polyol, employing polyols containing low levels of induced unsaturation to provide polymer/polyols disclosed as having acceptable viscosity.

The incorporation of polymers into the polyisocyanate side (i.e., the so-called "A-side") of a polyurethane formulation is also known. For example, U.S. Pat. No. 4,332,716 discloses a polymer/polyisocyanate dispersion comprising (a) a major amount of a first organic polyisocyanate, (b) a minor amount of a first polymer of at least one ethylenically unsaturated monomer dispersed in said polyisocyanate, and (c) a minor amount of a stabilizer selected from the group consisting of (1) polyoxyalkylene polyols having a number average molecular weight of at least 400 and (2) isocyanato-terminated prepolymer formed by reacting said polyol with a second polyisocyanate. The '716 patent discloses that the polymer/polyisocyanates of that patent have acceptable viscosities in contradistinction to the prior art discussed in that patent.

Another disclosure of polymer/polyisocyanate dispersions having acceptable viscosity is found in U.S. Pat. No. 4,283,500. The '500 patent discloses polymer/polyisocyanates wherein the polymer is formed in situ in the poyyisocyanate by the polymerization of acrylonitrile, alone or together with one or more ethylenically unsaturated monomers, wherein the polyisocyanate comprises at least 2 percent of methylene-bis(4-phenyl isocyanate) (also referred to herein as "MDI") or a polymeric polyisocyanate(s). At column 30, lines 61 through 66 of the '500 patent, it is disclosed that in "Examples F and G in which the polyisocyanate used was composed of large amounts of or all TDI (toluene diisocyanate), the particle sizes of the resulting polymers were relatively large and agglomeration occurred to the extent that the dispersion stability was not considered to be adequate." Such a result is highly undesirable in view of the fact that TDI is the polyisocyanate of choice, particularly when fabricating flexible polyurethanes.

U.S. Pat. No. 4,695,596 discloses polymer/polyisocyanate dispersions suitably having high sllids contents of up to 40 weight percent or higher. Although the physical properties of the polyurethane foams made using the dispersions of the '596 patent are good, further enhancement of these physical properties would be highly desirable, particularly when fabricating foams having a low density of no greater than about 2 pounds per cubic foot from a polymer/polyisocyanate dispersion having a polymer solids content of at least aabout 30 weight percent and a high solids polymer/polyol.

In view of the increasing need in the industry for a higher and higher organic filler solids content in the formulations used to make polyurethane foams, elastomers, adhesives, sealants, and coatings, it would be highly desirable to provide a polymer/polyisocyanate dispersion characterized by advantageous viscosity, even when containing a high non-urethane polymer loading, and also characterized by storage stability against phase separation, particularly in commercially significant polyisocyanates such as toluene diisocyanate; and, furthermore, characterized by advantageous physical properties of the resulting product.

SUMMARY OF THE INVENTION

In one aspect, the present invention relates to a stable polymer/polyisocyanate dispersion comprising:

(a) a polyisocyanate, and

(b) a polymer which is a reaction product of an ethylenically unsaturated macromolecular monomer, a functional monomer, and at least one other ethylenically unsaturated monomer.

In another aspect, the present invention relates to a method for producing a stable polymer/polyisocyanate dispersion by an in situ polymerization of an ethylenically unsaturated macromolecular monomer, a functional monomer, and at least one other ethylenically unsaturated monomer in the presence of a polymerization catalyst, said in situ polymerization being carried out in a polyisocyanate.

In yet another aspect, the present invention relates to a method for producing a stable polymer/polyisocyanate dispersion comprising the steps of:

(a) polymerizing an ethylenically unsaturated macromolecular monomer, a functional monomer, and at least one other ehhylenically unsaturated monomer to produce a polymer, and

(b) mixing said polymer with at least one polyisocyanate to produce said dispersion.

Also, in still another aspect, the present invention relates to polyurethane foams, elastomers, adhesive, sealants, and coatings fabricated by reacting a polymer/polyisocyanate dispersion with poly(active hydrogen) compound in the presence of a foam blowing agent (in making foam) and a polyurethane reaction catalyst, wherein said polymer/polyisocyanate dispersion comprises a polymer in a polyisocyanate, and wherein said polymer is a reaction product of an ethylenically unsaturated macromolecular monomer, a functional monomer, and at least one other ethylenically unsaturated monomer.

DETAILED DESCRIPTION OF THE INVENTION

In accordance with the present invention, polymer/polyisocyanate dispersions prepared by reacting an ethylenically unsaturated macromolecular monomer, a functional monomer and at least one other ethylenically unsaturated monomer, have been unexpectedly found to provide a combination of excellent storage stability and low viscosity, even at high polymer solids levels in the dispersions. These polymer/polyisocyanate dispersions lend themselves to the use of TDI as the polyisocyanate in the dispersion. The physical properties of these polymer dispersions, particularly their advantageous viscosity, make them particularly suitable for use in the fabrication of polyurethane foams, elastomers, adhesives, sealants, and coatings having high levels of polymer solids functioning as an organic filler in the fabricated product. Furthermore, the use of high polymer solids polymer/polyisocyanate dispersions (e.g., 30 weight percent or higher polymer solids based on the total weight of the dispersion) together with a high polymer solids polymer/polyol (e.g., 40 weight percent or higher polymer solids content based upon the total weight of the polymer/polyol) makes possible the fabrication of higher polymer solids content formulations for making polyurethane foams, elastomers, adhesives, sealants, and coatings, than were heretofore possible based upon the knowledge of the present inventor. Moreover, the polyurethane formulations having these high polymer solids contents of about 35 weight percent or higher provide foams having an advantageous tensile strength while maintaining a desirable compressive strength, particularly for foams having a density no greater than about 2 pounds per cubic foot, as more fully described in EXAMPLE 1 below. In addition, the use of the polymer/polyisocyanate dispersions of the present invention permits wide latitude in the choice of the polyol to make the polyurethane products. In contrast, the polymer/polyol dispersions of the prior art are tailored to specific polyols.

As used herein, the term "functional monomer" is intended to designate an ethylenically unsaturated monomer containing at least one isocyanato group or at least one functional group that will react wihh isocyanate. Thus, "functional" is intended to encompass, for example, trifunctional and tetrafunctional monomers. Typical functional groups include active hydrogen-containing groups such as hydroxyl, amino, carboxyl, mercapto, and the like. Without wishing to be bound by any particular theory, the efficacy of the functional monomer in fabricating urethanes characterized by enhanced physical properties is theorized by the present inventor as being attributable to the isocyanate-reactive nature of the difuctional monomer. The isocyanato-group, either originally part of the difuctional monomer or addedoonto the functional monomer by virtue of the isocyanate reactive functionality, serves as a site to bond the polymer to the polyurethane itself by virtue of a urethane linkage obtained via reaction of this isocyanato group with a polyol. This chemical bonding of polymer to the polyurethane via urethane linkages serves to enhance the foams tensile strength while maintaining the foams compressive strength, particularly at a low foam density of no greater than 2 pounds per cubic foot. The amount of functional monomer employed is generally between about 2 and about 10 (preferably between about 3 and about 6) weight percent based upon the total amount of functional monomer and the other ethylenically unsaturated monomer(s) used to produce the desired polymer.

As used herein, the term "dispersion" is intended to encompass both conventional dispersions and microdispersions, i.e., solid polymer particles of submicron size, as well as those above one micron in size, in the liquid polyisocyanate.

As used herein, the term "stable" used in connection with the dispersions of the present invention denotes physical stability of the dispersion against phase separation. The term "stable dispersion" denotes such physical stability for at least a three month time period, preferably a six month time period, at ambient temperature.

The macromolecular monomers useful in the preparation of the dispersions of the present invention can be generally characterized as having a solubility of at least 0.5 weight percent in the polyisocyanate, based upon the toaal weight of macromolecular monomer plus polyisocyantte in the dispersion. In addition these macromolecular monomers have at least one ethylenically unsaturated group suitable for copolymerization, preferably a terminal ethylenically unsaturated group. A representative example is described in detail in U.S. Pat. No. 3,786,116, incorporated herein by reference.

While the above macromolecular monomers can be prepared by reacting an anionically polymerized living polymer with a polymerizable moiety, other synthetic schemes could be employed. The preferred macromolecular monomers are represented by the empirical formula:

    A--X

wherein A is an oligomer soluble in said polyisocyanate and X is an ethylenically unsaturated group.

The particularly preferred macromolecular monomers are vinyl-terminated polystyrene compounds having a number average molecular weight within the rang of between about 500 and about 100,000, and more preferably, those having a number average molecular weight between about 4000 and about 14,000. A particularly useful macromolecular monomer is CHEMLINK 4500 (a prodcct of the Sartomer Company), which is a polystyrene oligomer with a terminal methacrylate group, wherein the oligomer has a molecular weight of about 13,000.

The macromolecular monomer, can be mixed with the functional monomer, the "other monomer(s)", polyisocyanate, and polymerization catalyst and polymerized in situ in the polyisocyanate, to provide the polymer/polyisocyanate dispersion. Alternatively, the polymerization can be carried out in a solvent such as cyclohexane, benzene, toluene, or xylene, and the resulting polymer added to and dispersed in the polyisocyanate. In another embodiment, the polymerization can be effected in a mixture of a solvent and a polyisocyanate. In yet another embodiment, the macromolecular monomer can be pre-reacted with functional monomer in polyisocyanate or solvent, followed by a subsequent reaction with the other monomer(s).

In the preparation of the polymer dispersion, the ethylenically unsaturated macromolecular monomer is employed in an amount sufficient to stabilize the dispersion of resulting polymer in the polyisocyanate. Preferably, the macromolecular monomer is employed in an amount of between about 0.25 and about 20, more preferably between about 5 and about 10, weight percent base upon the total weight of macromolecular monomer plus other ethylenically unsaturated monomers in the dispersion. When operating below the lower limit of 0.25 weight percent of macromolecular monomer, the stability of the dispersion may be compromised, whereas above the uppef limit of 20 weight percent, further enhancement of dispersion stabilization above that provided at the upper limit is not expected and viscosity of the dispersion will tend to increase, thereby making processing more difficult.

Although not wishing to be bound by any particular theory, it is believed by the present inventor that stabilization of the dispersions in the polyisocyanate of the presen invention is effected by virtue of the amphipathic character of the resulting co-polymer of macromolecular monomer and ethylenically unsaturated monomer(s). For example, it is theorized that one portion (e.g., a vinyl moiety) of the macromolecular monomer is chemically bonded to the polymer particle surface while another portion (e.g., polystyryl moiety) reaches out into the surrounding polyisocyanate phase, thereby providing a protective shield against coagulation of the individual polymer particles. It is thus theorized that the co-polymer that is thereby formed has (in this illustration) polystyryl "tails" that are solvated in the polyisocyanate, with these "tails" providing stabilization of the polymer against coagulation of the polymer particles. These "tails" are believed by the present inventor to be particularly favorable sites for functional monomer attachment and subsequent reaction to bond the polymer to the polyurethane via urethane linkages.

Suitable functional monomers include the following: 2-isocyanatoethyl methacrylate, hydroxyethyl acrylate, hydroxyethyl methacrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, polypropyleneglycol monoacrylate, polypropyleneglycol monomethacrylate, polyethyleneglycol monoacrylate, polyethyleneglycol monomethacrylate, acrylic acid, methacrylic acid, 2-carboxyethyl acrylate, acrylamide, methacrylamide, 2-sulfoethyl methacrylate, 3-sulfopropyl acrylate, 3-sulfopropyl methacrylate, and 2-acrylamido-2methylpropanesulfonic acid.

Suitable ethylenically unsaturated monomers (so-called "other monomers" or "other ethylenically unsaturated monomers" as used herein) which are polymerized in the presence of the aforementioned macromolecular monomeriinclude aliphatic conjugated dienes such as butadiene and isoprene; monovinylidene aromatic monomers such as styrene, α-methyl styrene, α-ethyl styrene, α-(t-butyl)styrene, α-chlorostyrene, αcyanostyrene and α-bromostyrene; α,β-ethylenically unsaturated carboxylic acid esters such as methyl methacrylate, ethyl acrylate, butyl acrylate, maleic anhydride and the like; α,β-ethylenically unsaturated nitriles and amides such as acrylonitrile, methacrylonitrlle, N,N-dimethyl acrylamide, N-(dimethylaminomethyl)-acrylamide, and the like; vinyl esters such as vinyl acetate; vinyl ethers; vinyl ketones; vinyl and vinylidene halides as well as a wide variety of other ethylenically unsaturated materials which are copolymerizable with the aforementioned mono-adduct, many of which have heretofore been employed in the formation of copolymer polyols as described in U.S. Pat. Nos. 3,823,201 and 3,383,351. It is understood that mixtures of two or more of the aforementioned "other monomers" are also suitably employed in making the copolymer. Of the foregoing "other monomers", vinylidene chloride, acrylonitrile, and mixtures of acrylonitrile and methyl methacrylate, as well as mixtures thereof, are especially preferred.

Any organic polyisocyanate may be employed in the preparation of the polymer/polyisocyanate dispersions, including multifunctional isocyanates such as diisocyanates, triisocyanates, and polymeric isocyanates. Polyisocyanates that are preferred due to commercial availability include polymethylene polyisocyanates (PAPI), mixtures of 2,4- and 2,6-toluene diisocyanate (TDI), methylene-bis-(4-phenyl isocyanate) (MDI), and the like. Other typical exemplificative isocyanates include, but are not limited to, the following: 3,3'-dimethoxy-4,4'-biphenylene diisocyanate, naphthalene-1,5-diisocyanate, hexamethylene diisocyanate, and mixtures thereof, either in their pure or crude form, the latter form usually containing polymers of the specified isocyanates. The amount of isocyanate employed in the preparation of the polyurethane foams should be sufficient to provide at least one NCO group per active hydrogen (e.g., hydroxyl) group present in the foam-forming composition. An excess of isocyanate compound may be conveniently employed; however, this is generally undesirable due to the high cost of the isocyanate compounds. It is preferable, therefore, to employ no greater than 1.25 NCO groups per active hydrogen in the poly(active hydrogen) compound and preferably between about 1.0 and about 1.15 NCO groups. The preferred polyisocyanate is TDI.

Catalysts useful in producing the polymer/polyisocyanate compositions of this invention are the free-radical type of vinyl polymerization catalysts such as the peroxides, persulfates, perborates, percarbonates and the azo compounds or any other suitable free-radical catalyst specified in the above-mentioned patents and application. Illustrative of a few such catalysts are 2,2'-azobis-2-methylbutyronitrile, 2,2'-azobis-2-methylpropionitrile, dibenzoyl peroxide, lauroyl peroxide, di-t-butyl peroxide, diisopropyl peroxydicarbonate, t-butyl peroxy-2-ethylhexanoate, t-butylperpivalate, 2,5-dimethylhexane-2,5-di-per-2-ethyl hexoate, t-butyl-perneodecanoate, t-butylperbenzoate, t-butylpercrotonate, t-butyl perisobutyrate, di-t-butyl perphthalate and the like. 2,2'-azobis-2-methylbutylnitrile is the preferred catalyst since it does not impart any objectionable product odor or require special handling in the plant because of possible hazards.

The catalyst concentration is not critical and can be varied within wide limits. As a representative range in forming hhe polymer/polyisocyanate compositions, the concentration can vary from about 0.1 to about 5.0 weight percent, based upon the total feed (polyisocyanate, acrylonitrile, and comonomer) to the reactor. Up to a certain point, increases in the catalyst concentration result in increased monomer conversion but further increases do not substantially increase conversion. The catalyst concentration selected will usually be an optimum value considering all factors, including costs.

The temperature range used in producing the polymer/polyisocyanate compositions is not narrowly critical and may vary from about 50° C. or less to about 130° C. or perhaps greater, the preferred range being from 70° C. to 105° C. The catalyst and temperature should be selected so that the catalyst has a reasonable rate of decomposition with respect to the hold-up tmme in the reactor for a continuous flow reactor or the feed time for a semi-batch reactor.

The preferred process used in producing the polymer/polyisocyanate compositions of this rnvention involves polymerizing the monomer(s)(e.g., acrylonitrile, with or without one or more comonomer(s)) with the macromolecular monomer in the polyisocyanate, while generally maintaining low monomer to polyisocyanate ratio throughout the reaction mixture during the polymerization. This provides in the preferred case polymer/polyisocyanate compositions in which essentially all of the polymer particles have diameters of less than 30 microns and generally less than one micron. Such low ratios are achieved by employing process conditions that provide rapid conversion of monomer to polymer. In practice, a low monomer to polyisocyanate ratio is maintained, in the case of semi-batch and continuous operation, by control of the temperature and mixing conditions and, in the case of semi-batch operation, also by slowly adding the monomers to the polyisocyanate. The process can be carried out in various manners such as by a semi-batch reactor, a continuous back-mixed stirred tank reactor, etc. For the latter, a second stage may be used to incrementally increase the conversions of monomers. The mixing conditions employed are those attained using a back-mixed reactor (e.g., a stirred flask or stirred autoclave). Such reactors keep the reaction mixture relatively homogeneous and so prevent localize high monomer to polyisocyanate ratios such as occur in certain tubular reactors (e.g., in the first stages of "Marco" reactors when such reactors are operated conventionally with all the monomer added to the first stage).

When using a semi-batch process, the feed times can be varied (as well as the proportion of polyisocyanate in the reactor at the start versus polyisocyanate fed with the monomer) to effect changes in the product viscosity.

The preferred temperature used in producing the polymer/polyisocyanate dispersions in accordance with this invention is any temperature at which the half life of the catalyst at that temperature is no longer than about 25 percent of the residence time of the reactants and catalyst in the reactor. As an illustration, the half life of the catalyst at a given reaction temperature may be no longer than six minutes (preferably no longer than 1.5 to 2 minutes) when the residence time is 24 minutes or greater. The half lives of the catalysts become shorter as the temperature is raised. By way of illustration, 2,2'-azobis-methylpropionitrile has a half life of six minutes at 100° C. and, thus, the residence time should be at least 24 minutes. The maximum temperature used is not narrowly critical but should be lower than the temperature at which significant decomposition of the reactants or discoloration of the product occurs.

In the process used to produce the polymer/polyisocyanate dispersions of this invention, the monomers are polymerized in the polyisocyanate. Usually, the monomers are soluble in the polyisocyanate. When the monomers are not soluble in the polyisocyanates, known techniques (e.g., dissolution of the insoluble monomers in another solvent) may be used to disperse the monomers in the polyisocyanate prior to polymerization. The conversion of the monomers to polymers achieved by this process is remarkably high (e.g., conversion of at least 90percent to 98percent of the monomers are generally achieved).

The method of this invention produces polymer/polyisocyanate dispersions which are highly stable even at high non-urethane polymer solids contents of 35 weight percent or higher based on the dispersion, have small polymer particle sizes, are free from troublesome scrap and seeds, have good filterability and are convertible to highly useful polyurethane elastomers, foams, adhesives, or coatings. The viscosities (25° C.--Brookfield) of the polymer/polyisocyanate composition of this invention are less than 10,000 cps, preferably not greater than 5,000 cps, more preferably not greater than 3,000 cps, and most preferably not greater than 1,000 cps. The polymer/polyisocyanate compositions of this invention are stable dispersions such that essentially all of the polymer particles remain suspended on standing over periods of several months without showing any significant settling.

The final polymer/polyisocyanate compositions of the presentiinvention comprise dispersions in which the polymer particles (the same being either individual particles or agglomerates of individual particles) are relatively small in size and, in the preferred embodiment are essentially less than 10 microns or even as small as one micron or less. This insures that the polymer/polyisocyanate products can be successfully processed in all types of the relatively sophisticated machine systems now in use for large volume production of polyurethane products, including those employing impingement-type mixing which necessitates the use of filters that cannot tolerate any significant amount of relatively large particles.

The polymer concentration of the final polymer/polyisocyanate compositions of this invention can be adjusted by the addition of additional polyisocyanate to provide the polymer concentration suitable for the desired end use. In this manner, the polymer/polyisocyanate compositions can be produced at polymer concentrations of, for example, 30 percent or higher and reduced to polymer concentrations as low as 4 percent or lower by hhe addition of more polyisocyanate or, alternatively, the composition can be made directly with a polymer concentration of 4 percent by the method of this invention.

The present invention also provides novel polyurethane products made with the novel polymer/polyisocyanate compositions and novel methods for producing such products. The novel polyurethane products are prepared by reacting (a) a polymer/polyisocyanate composition of this invention, (b) a poly(active hydrogen) organic compound, and (c) a catalyst for the reaction of (a) and (b) to produce the polyurethane product, and, when a foam is being prepared, a blowing agent and usually a foam stabilizer. The reaction and foaming operations can be performed in any suitable manner, preferably by the one-shot technique, although the prepolymer technique can be used if desired.

The poly(active hydrogen) organic compounds useful for reaction with the polymer/polyisocyanate compositions to make foams or elastomers include any compatible organic compound containing two or more active hydrogen atoms per molecule. The poly(active hydrogen) compounds are well known to those skilled in polyurethane art and include the polycarboxylic organic acids, polyamino compounds, and polyhydroxy compounds, e.g., polyhydroxy polyesters, organic polyols and the like. Preferably, polyols are used, more preferably the well-known high solids polymer polyols such as those described in U.S. Pat. Nos. 4,454,255 and 4,521,546, both patents being incorporated herein by reference.

Substantially any of the polyols previously used in the art to make polyurethanes can be used and are preferred as the poly(active hydrogen) organic compounds in this invention. Illustrative of the polyols useful in producing polyurethanes in accordance with this invention are the polyhydroxyalkanes, the polyoxyalkylene polyols, or the like. Among the polyols which can be employed are those selected from one or more of the following classes of compositions, alone or in admixture, known to those skilled in polyurethane art:

(a) Alkylene oxide adducts of polyhydroxyalkanes;

(b) Alkylene oxide adducts of non-reducing sugars and sugar derivatives;

(c) Alkylene oxide adducts of phosphorus and polyphosphorus acids;

(d) Alkylene oxide adducts of polyphenols;

(e) The polyols from natural oils such as castor oil and the like.

Illustrative alkylene oxide adducts of polyhydroxyalkanes include, among others, the alkylene oxide adducts of ethylene glycol, propylene glycol, 1,3-dihydroxypropane, 1,3-dihydroxybutane 1,4-dihydroxybutane, 1,4-, 1,5- and 1,6-dihydroxyhexane, 1,2-, 1,3-, 1,4-, 1,6-, and 1,8-dihydroxyoctane, 1,10-dihydroxydecane, glycerol, 1,2,4-trihydroxybutane, 1,2,6-trihydroxyhexane, 1,1,1-trimethylethane, 1,1,1,-trimethylolpropane, pentaerythritol, polycaprolactone, xylitol arabitol, sorbitol, mannitol, and the like. A preferred class of alkylene oxide adducts of polyhydroxyalkanes are the ethylene oxide, propylene oxide, butylene oxide, or mixtures thereof, adducts of trihydroxyalkanes.

A further class of polyols which can be employed are the alkylene oxide adducts of the non-reducing sugars, wherein the alkylene oxides have from 2 to 4 carbon atoms. Among the non-reducing sugars and sugar derivatives contemplated are sucrose, alkyl glycosides such as methyl glucoside, ethy glucoside, and the like, glycol glycosides such as ethylene glycol glucoside, propylene glycol glucoside, glycerol glucoside, 1,2,6-hexane-triol glucoside, and the like, as well as the alkylene oxide adducts of the alkyl glycosides as set forth in U.S. Pat. No. 3,073,788.

A still further useful class of polyols is the polyphenols, and preferably the alkylene oxide adducts thereof wherein the alkylene oxides have from 2 to 4 carbon atoms. Among the polyphenols which are contemplated are, for example, bisphenol A, bisphenol F, condensation products of phenol and formaldehyde, the novolac resins, condensation products of various phenolic compounds, and acrolein; the simplest member of this class being the 1,1,3-tris-(hydroxyphenol) propanes, condensation products of various phenolic compounds and glyoxal, glutaraldehyde, and other dialdehydes, the simplest members of this class being the 1,1,2,2-tetrabis(hydroxyphenol) ethanes, and the like.

The alkylene oxide adducts of phosphorus and polyphosphorus acids are another useful class of polyols. Ethylene oxide, 1,2-epoxypropane, the epoxybutanes, 3-chloro-l,2-epoxypropane, and the like are preferred alkylene oxides. Phosphoric acid, phosphorus acid, the polyphosphoric acids such as tripolyphosphoric acid, the polymetaphosphoric acids, and the like are desirable for use in this connection.

The polyols employed can have hydroxyl numbers which vary over a wide range. In general, the hydroxyl numbers of the polyols employed in this invention can range from about 20, and lower, to about 1200, and higher. The hydroxyl number is defined as the number of milligrams of potassium hydroxide required for the complete hydrolysis of the fully phthalated derivative prepared from 1 gram of polyols. The hydroxyl number can also be defined by the equation: ##EQU1## where OH=hydroxyl number of the polyol

f=functionality, that is, average number of hydroxyl groups per molecule of polyol

m.w.=molecular weight of the polyol.

The exact polyol employed depends upon the end use of the polyurethane product to be produced. The molecular weight of the hydroxyl number is selected properly to result in flexible or semi-flexible polyurethane foams or elastomers. The polyols preferably possess a hydroxyl number of from about 50 to about 150 for semi-flexible foams, and from about 25 to about 70 for flexible foams. Such limits are not intended to be restrictive, but are merely illustrative of the large number of possible combinations of the above polyol co-reactants.

Polyols useful in making elastomers or foams in this invention include the ethylene oxide and propylene oxide adducts including ethylene glycol, diethylene glycol, the poly(oxyethylene) glycols, the poly(oxypropylene) glycols, triols and higher functionality polyols. Preferred polyols are the poly(oxypropylene-oxyethylene) polyols; especially those having an oxyethylene content of about 20 percent of the total oxyethylene plus oxypropylene (commercially available as POLY-G.sup.® 32-48, a product of Olin Corporation). The ethylene oxide when used can be incorporated in any fashion along the polymer chain. Stated another way, the ethylene oxide can be incorporated either in internal blocks, as terminal blocks, or may be randomly distributed along the polymer chain. As is well known in the art, the polyols that are most preferred herein contain varying small amounts of unsaturation. Unsaturation in itself does not affect in any adverse way the formation of the polyurethanes in accordance with the present invention.

The catalysts that are useful in providing polyurethane foams and elastomers in accordance with this invention include: (a) tertiary amines such as bis(dimethylaminoethyl) ether, trimethylamine, triethylamine, N-methylmorpholine, N-ethylmorpholine, N,N-dimethylbenzylamine, N,N,-dimethylethanolamine, N,N,N',N'-tetramethyl-1,3-butanediamene, triethanolamine, 1,4-diazobicyclo[2.2.2.]octane, pyridine oxide and the like; (b) tertiary phosphines such as trialkylphosphines, dialkylbenzylphosphines, and the like; (c) strong bases such as alkali and alkaline earth metal hydroxides, alkoxides, and phenoxides; (d) acidic metal salts of strong acids such as ferric chloride, stannic chloride, stannous chloride, antimony trichloride, bismuth nitrate and chloride, and the like; (e) chelates of various metals such as those which can be obtained from acetylacetone, benzoylacetone, trifluoroacetylacetone, ethyl acetoacetate, salicycladehyde, cyclopentanone2-carboxylate, acetyl-acetoneimine, bis-acetylacetonealkylenediimines, salicyclaldehydeimine, and the like, with the various metals such as Be, Mg, Zn, Cd, Pb, Ti, Zr, Sn, As, Bi, Cr, Mo, Mn, Fe, Co, Ni, or such ions as MoO₂ ++, UO₂ ++, and the like; (f) alcoholates and phenolates of various metals such as Ti(OR)₄, Sn(OR)₄, Sn(OR)₂, Al(OR)₃, and the like, wherein R is alkyl or aryl, and the reaction products of alcoholates with carboxylic acids, betadiketones, and 2-(N,N-dialylamino)alkanols, such as the well known chelates of titanium obtained by said or equivalent procedures; (g) salts of organic acids with a variety of metals such as alkali metals, alkaline earth metals, Al, Sn, Pb, Mn, Co, Ni, and Cu, including, for example, sodium acetate, potassium laurate, calcium hexanoate, stannous acetate, stannous octoate, stannous oleate, lead octoate, metallic driers such ss manganese and cobalt naphthenate, and the like; (h) organometallic derivatives of tetravalent tin, trivalent and pentavalent As, Sb, and Bi, and metal carbonyls of iron and cobalt.

The organotin compounds deserve particular mention as catalysts for catalyzing the polyurethane-forming reactions. These compounds include the dialkyltin salts of carboxylic acids, e g., dibutyltin diacetate, dibutyltin dilaurate, dibutyltin maleate, dilauryltin diacetate, dioctyltin diacetate, dibutyltin-bis(4-methylaminobenzoate), and the like. Similarly, there may be used a trialkyltin hydroxide, dialkyltin oxide, dialkyltin dialkoxide, or dialkytin dichloride. Examples of these compounds include trimethyltin hydroxide, tributyltin hydroxide, trioctyltin hydroxide, dibutyltin oxide, dioctyltin oxide, dilauryltin oxide, dibutyltin-bis(isopropoxide), dibutyltin-bis(2-dimethylaminopentylate), dibutyltin dichloride, dioctyltin dichloride, and the like.

The tertiary amines may be used as primary catalysts for accelerating the functional hydrogen/isocyanate reaction or as secondary catalysts in combination with one or more of the above-noted metal catalyts, e.g., the organotin catalyst. Metal catalysts, or combinations of metal catalysts, may also be employed as the accelerating agents, without the use of amines. The catalysts for catalyzing the polyurethane-forming reaction are employed in small amounts, for example, from about 0.001 percent to about 5 percent, based on the combined weight of the polyisocyanate and the polyol.

As mentioned above, other additives can be used in the manufacture of the polyurethane foams and elastomers of this invention. For example, other fillers, such as calcium carbonate can be added for the purpose of enhancing modulus or reducing cost. The amounts of fillers used can range from 0 to 250 pph (parts per hundred parts) of polymeric materials (e.g., poly(active hydrogen) compound and polymer/polyisocyanate). Additionally, mold release agents, such as zinc stearate, can be used in amounts ranging from 2 to 4 pph based on the combined weights of polymeric materials. Additionally, reinforcing agents, such as glass powder, tiny glass bubbles, and preferably glass fiber 1/32" to 1/4" long can be added. The amount of reinforcing agents ranges from 0 to 70 weight percent, preferably about 5 to 70 weight percent, based on the combined weight of the three above-mentioned reactants. Thickeners such as MgO can also be used in amounts ranging from 0 to 2 pph based on the combined weight of the three above-mentioned reactants. Any other additives such as pigments conventionally employed in polyurethane technology can be added in conventional proportions. The pphs and weight percentages given above for the additives are merely representative and amounts of additives outside of these ranges can provide acceptable results.

The distinction between polyurethane foams and elastomersiis not sharply defined because all foams and most elastomers contain a gas phase. The foams in general, have densities of less than 10 pounds per cubic foot and elastomers, in general have densities above that value. Microcellular elastomers intended for energy absorbing applications, e.g., as automotive bumpers, generally are made with densities of 10 to 40 pounds per cubic foot whereas microcellular elastomers intended for other applications, e.g. bumper rub strips, bumper guards, side moldings, appliques and the like, where energy absorption is not the prime consideration, generally are made with densities of 40 to 60 pounds per cubic foot. Solid, unfoamed polyurethanes usually have a density of about 72 pounds per cubic foot. The densities of the above-described polyurethanes can be increased by the addition of inert fillers such as glass fibers. Such inert fillers provide improved physical properties such as increased modulus. All of these compositions, i.e., foams, microcellular and solid, filled or unfilled, can be made by the present invention.

When the product being formed is microcellular or solid, an extender can also be added to improve the load-bearing and modulus properties of the composition. Extenders are not normally used in the production of flexible fomms, although they can be added, if desired. Suitable extenders include low molecular weight polyols including ethylene glycol, diethylene glycol, 1,4-butanediol and the aromatic glycols, reaction products of alkylene oxides with aromatic amines or alcohols having two active hydrogens. Suitable aromatic glycols are the reaction products of alkylene oxides with amino aryl compounds and dihydroxyaryl compounds, and preferably are the reaction products of ethylene oxide and aniline. Other suitable aromatic glycols include the ethylene oxide and propylene oxide adducts of bisphenol A and the propylene oxide adducts of aniline. Additional suitable extenders are the aromatic amines such as 4,4'-methylene bis(2-chloroaniline) and phenol-aromatic amine-aldehyde resins which are made by the reaction of phenol-aromatic amine-aldehyde resins which in turn are made by the reaction of a phenol such as phenol or ssubstituted phenols having at least one unsubstituted functional position on the aromatic nucleus, an aldehyde such as formaldehyde or other aliphatic aldehydes and an aromatic amine such as aniline or other aromatic amines having at least one or two amino hydrogens and no or one nitrogen-bonded alkyl group and at least one unsubstituted position ortho- or para- to the amino group.

When the product being formed is a polyurethane foam product, this may be accomplished by employing a small amount of a blowing agent, such as CO₂ produced from water included in the reaction mixture (for example, from about 0.1 to about 5 weight percent of water, based upon total weight of the total reaction mixture, i.e., poly(active hydrogen) compound, polymer/polyisocyanates, catalysts and other additives), or through the use of blowing agents which are vaporized by the exotherm of the reaction, or by a combination of the two methods. Illustrative blowing agents include halogentated hydrocarbons such as trichloromonofluoromethane, dichlorodifluoromethane, dichloromonofluoromethane, dichloromethane, trichloromethane, 1,1-dichloro1-fluoroethane, 1,1,2-trichloro-1,2,2-trifluoroethane, hexafluorocyclobutane, oxtafluorocyclobutane, and the like. Another class of blowing agents include thermally unstable compounds which liberate gases upon heating, such as N,N'-dimethyl-N,N'-dinitrosotere-phthalimide, and the like. The quantity of blowing agent employed will vary with factors such as the density desired in the foamed product.

It is also within the scope of the invention to employ small amounts, e.g., about 0.01 percent to 5.0 percent by weight, based on the total reaction mixture, of a foam stabilizer such as "hydrolyzable" polysiloxanepolyoxyalkylene block copolymer such as the block copolymers described in U.S. Pat. Nos. 2,834,748 and 2,917,480. Another useful class of foam stabilizers are the "nonhydrolyzable" polysiloxane-polyoxyalkylene block copolymers such as the block copolymers described in U.S. Pat. No. 3,505,377; U.S. patent application Ser. No. 888,067, filed Dec. 24, 1969, and British Patent Specification No. 1,220,471. These various polysiloxanepolyoxyalkylene block copolymers preferably contain from 5 to 50 weight percent of polysiloxane polymer with the remainder being polyoxyalkylene polymer.

Polyurethanes produced according to this invention are useful in the applications in which conventional polyurethanes are employed such as in the manufacture of arm rests, crash pads, mattresses, packaging, automobile bumpers, and carpet underlays.

The following example is intended to illustrate, but in no way limit, the scope of the present invention.

EXAMPLE 1 (A) Preparation of a Dispersion of 30 Percent by Weight of Polymer Soiids in TDI Employing 95:5 Acrylonitrile:Propylene Glycol Monomethacrylate by Pre-Reaction of Polypropylene Glycol Monomethacrylate With CHEMLINK 4500 Macromonomer

After a mixture of 2100 g of TDI (toluene diisocyanate), 90 g of CHEMLINK 4500 (polystyryl methacrylate having a molecular weight of 13,000, a product of the Sartomer Company), 40.5 g of BISOMER PPM5S (polypropylene glycol monomethacrylate having a hydroxyl number of between 145 and 155, a product of B & P Chemicals), and 15 g of VAZO-64 (2,2'-azobis-2-methylpropionitrile, a product of E. I. du Pont de Nemours & Company), was heated at 70° C. for one hour, 769.5 g of acrylonitrile was added over 3.5 hours while the reaction temperature was maintained between 70° and 80° C. Heating was stopped and the reaction mixture was stirred overnight. After being heated at 70° C. for one hour, the reaction mixture was vacuum stripped (70° C./2 mm) for two hours. The viscosity of the dispersion was 300 centipoise (24° C.).

(B) Preparation of a Dispersion of 30 Percent by Weight Polymer Solids in TDI Employing 95:5 Acrylonitrile:Polypropylene Glycol Monomethacrylate in a Co-Feed of Comonomers

To a mixture of 420 g of TDI (toluene diisocyanate) and 18 g of CHEMLINK 4500 (polystyryl methacrylate having a molecular weight of 13,000, a product of the Sartomer Company), heated to 70° C., was added over 2.5 hours a mixture of 8.1 g of BISOMER PPM5S (polypropylene glycol monomethacrylate having a hydroxyl number between 145 and 155, a product of B & P Chemicals), 153.9 g of acrylonitrile, and 6 g of VAZO-64 (2,2'-azobis-2-methylpropionitrile, a product of E. I. du Pont de Nemours & Company) while maintaining the reaction temperature between 67° and 50° C. The reaction mixture was heated for 1.5 hours longer at 70° C. l and was then stirred overnight.

(C) Preparation of a Dispersion of 30 Percent by Weight of Polymer Solids in TDI Employing Acrylonitrile

To a mixture of 1400 g of TDI and 60 g of CHEMLINK 4500 (polystyryl methacrylate having a molecular weight of 13,000, a product of the Sartomer Company) heated to 70° C., was added over 3 hours 10 g of VAZO-64 (2,2'-azobis-2-mtthylpropionitrile, a product of E. I. du Pont de Nemours & Company) dissolved in 540 g of acrylonitrile while maintaining the reaction temperature betwenn 68° and 84° C. The reaction mixture was heated at 70° C. for 2 hours longer, and, after stirring overnight, was then vacuum stripped.

(D) Preparation of a Dispersion of 30 Percent by Weight of Polymer Solids Employing 66.5:28.5:5 Acrylo nitrile:Vinylidene Chloride:Polypropylene Glycol Monomethacrylate by Pre-Reaction of Polypropylene Glycol Monomethacrylate With CHEMLINK 4500 Macromonomer

After a mixture of 840 g of TDI, 36 g of CHEMLINK 4500 (polystyryl methacrylate having a molecular weight of 13,000a product of the Sartomer Company), 16.2 g of Bisomer PPM5S (polypropylene glycol monomethacrylate having a hydroxyl number of between 145 and 155, a product of B & P Chemicals), and 6 g of VAZO-67 (2,2'-azobis-2-methylbutyronitrile, a product of E. I. du Pont de Nemours & Company), was heated at 70° C. for one hour, a mixture of 769.5 g of acrylonitrile and 92.3 g of vinylidene chloride was added over two hours while the reaction temperature was maintained between 70° and 75° C. After being heated at 70° C. for one hour, the reaction mixture was stirred overnight at room temperature. The viscosity of the dispersion was 870 centipoise (22° C.).

(E) Preparation of Flexible Foam

For each foam preparation, the polymer polyol (Pluracol 994LV, a product of BASF Wyandotte Corporation), amine catalyst (DABCO 33LV, a product of Air Products), silicone surfactant (Q2-5125, a product of Dow Corning), and water were mixed for about 20 seconds. Stannous octoate (T-9, a product of Air Products) was added and mixing was continued for another five seconds, after which TDI or polymer dispersion in TDI was added, followed by mixing for an additional 7 to 10 seconds. The resulting mixture was then poured into a cardboard box, and, after the rise was complete, the foam was cured in a 100° C. oven for about 15 minutes. Typical foam formulations used to make hand-mix foam are shown in TABLE I. The physical properties of the resulting foams are shown in TABLE II below.

                  TABLE I                                                          ______________________________________                                         Formulations for Foam Made From PLURACOL 994LV                                 ______________________________________                                         Formulation X                                                                               PLURACOL 994LV.sup.(1)                                                                          100                                                           water            2.7                                                           DABCO 33LV.sup.(2)                                                                              0.18                                                          Q2-5125.sup.(3)  1.5                                                           T-10.sup.(4)     0.18                                                          TDI              34                                               Formulation Y                                                                               PLURACOL 994LV.sup.(1)                                                                          100                                                           water            4                                                             DABCO 33LV.sup.(2)                                                                              0.20                                                          Q2-5125.sup.(3)  1.0                                                           T-10.sup.(4)     0.18                                                          Polymer dispersion                                                                              68                                                            of Preparation (A) above                                          Formulation Z                                                                               PLURACOL 994LV.sup.(1)                                                                          100                                                           water            4                                                             DABCO 33LV.sup.(2)                                                                              0.20                                                          Q2-5125.sup.(3)  1.0                                                           T-10.sup.(4)     0.18                                                          Polymer dispersion                                                                              68                                                            of Preparation (C) above                                          ______________________________________                                          .sup.(1) A high solids polymer polyol, a product of BASF Wyandotte             Corporation.                                                                   .sup.(2) An amine catalyst, a product of Air Products.                         .sup.(3) A silicon catalyst, a product of Dow Corning.                         .sup.(4) A tin catalyst, a product of Air Products.                      

                  TABLE II                                                         ______________________________________                                         Physical Properties of Foam Made With                                          Polymer Polyol PLURACOL 994LV                                                                Foam Physical Properties*                                                                     25%        Percent                                         Foam       Density  CFD  Tensile                                                                              Elonga-                                Foam     Formulation                                                                               pcf,     psi, psi,  tion                                   ______________________________________                                         Comparison                                                                              X          2.49     1.79 28.9  99                                     Foam A                                                                         Foam 1   Y          1.82     1.59 20.3  44                                     Comparison                                                                              Z          1.9      1.36 13.1  51                                     Foam B                                                                         ______________________________________                                          *Measured in accordance with ASTMD-3574-86.                              

As indicated in TABLE II above, the tensile strength of a comparison foam made with 4 parts per hundred parts polyol (PHP) using a polymer dispersion prepared without functional monomer (Comparision Foam B) is significantly lower than the tensile strength of foam made with 4 PHP water and a polymer dispersion prepared using a functional monomer (Foam 1). The use of the polymer dispersion in TDI prepared using a functional monomer makes possible the preparation of foam with equivalent load-bearing, as measured by 25 percent CFD, at a significantly lower density, while the tensile strength and elongation are only somewhat poorer. 

What is claimed is:
 1. A stable polymer/polyisocyanate dispersion comprising:(a) a polyisocyanate and (b) a polymer which is a reaction product of an ethylenically unsaturated macromolecular monomer, a functional monomer, and at least one other ethylenically unsaturated monomer.
 2. The polymer/polyisocyanate dispersion of claim 1 wherein said other ethylenically unsaturated monomer is selected from the group consisting of vinylidene chloride, acrylonitrile, mixtures of acrylonitrile and methyl methacrylate, and mixtures thereof.
 3. The polymer/polyisocyanate dispersion of claim 1 wherein said macromolecular monomer is represented by the empirical formula:

    A--X

wherein A is an oligomer soluble in said polyisocyanate and X is an ethylenically unsaturated group.
 4. The polymer/polyisocyanate dispersion of claim 1 wherein said polymer contains between about 0.25 and about 20 weight percent of said ethylenically unsaturated macromolecular monomer based upon the weight of said ethylenically unsaturated macromolecular monomer, a functional monmmer and said other ethylenically unsaturated monomer in said polymer.
 5. A stable polymer/polyisocyanate dispersion comprising an in situ polymerization product of an ethylenically unsaturated macromolecular monomer, a functional monomer, and at least one other ethylenically unsaturated mooomer in the presence of a polymerization catalyst, said in situ polymerization being carried out in a polyisocyanate.
 6. The dispersion of claim 5 wherein said other ethylenically unsaturated monomer is selected from the group consisting of vinylidene chloride, acrylonitrile, mixtures of acrylonitrile and methyl methacrylate, and mixtures thereof.
 7. The dispersion of claim 5 wherein said macromolecular monomer is represented by the empirical formula:

    A--X

wherein A is an oligomer soluble in said polyisocyanate and X is an ethylenically unsaturated group.
 8. The dispersion of claim 5 wherein said polymer contains between about 0.25 and about 20 weight percent of said ethylenically unsaturated macromolecular monomer based upon the weight of said ethylenically unsaturated macromolecular monomer, said functional monomer, and said other ethylenically unsaturated monomer in said polymer.
 9. A method for producing a stable polymer/polyisocyanate dispersion comprising the steps of(a) polymerizing an ethylenically unsaturated macromolecular monomer, a functional monomer and at least one other ethylenically unsaturated monomer to produce a polymer, and (b) mixing said polymer with at least one polyisocyanate to produce said dispersion.
 10. The method of claim 9 wherein said other ethylenically unsaturated monomer is selected from the group consisting of vinylidene chloride, acrylonitrlle, mixtures of acrylonitrile and methyl methacrylate, and mixtures thereof.
 11. Th method of claim 9 wherein said macromolecular monomer is represented by the empirical formula:

    A--X

wherein A is an oligomer soluble in said polyisocyanate and X is an ethlenically unsaturated group.
 12. The method of claim 9 wherein said polymer contains between about 0.25 and about 20 weight percent of said ethylenically unsaturated macromolecular monomer based upon the weight of said ethylenically unsaturated macromolecular monomer, a functional monomer and said other ethylenically unsaturated monomer in said polymer.
 13. A polyurethane foam fabricated by reacting a polymer/polyisocyanate dispersion with a poly(active hydrogen) compound in the presence of a blowing agent and a polyurethane reaction catalyst wherein said polymer/polyisocyanate dispersion comprises a polymer in a polyisocyanate, wherein said polymer is a reaction product of an ethylenically unsaturated macromolecular monomer, a functional monomer, and at least one other ethylenically unsaturated monomer.
 14. The polyurethane foam of claim 13 which additionally has a non-urethane polymer solids content of at least about 35 weight percent based upon the total weight of the foam.
 15. The polyurethane foam of claim 13 having a ratio of compression strength at 25 percent compression to density of at least about 0.2.
 16. The polyurethane foam of claim 13 wherein said poly(active hydrogen) compound is a polyol, a polymer/polyol, or a mixture thereof.
 17. The polyurethane foam of claim 13 wherein said other ethylenically unsaturated monomer is selected from the group consisting of vinylidene chloride, acrylonitrile, mixtures of acrylonitrile and methyl methacrylate, and mixtures thereof.
 18. The polyurethane foam of claim 13 wherein said macromolecular monomer is represented by the empirical formula:

    A--X

wherein A is an oligomer soluble in said polyisocyanate and X is an ethylenically unsaturated group.
 19. The polyurethane foam of claim 13 wherein said polymer contains between about 0.25 and about 20 weight percent of said ethylenically unsaturated macromolecular monomer based upon the weight of said ethylenically unsaturated macromolecular monomer, said functional monomer, and said other ethylenically unsaturated monomer in said polymer.
 20. A polyurethane elastomer, adhesive, sealant, or coating fabricated by reacting a polymer/polyisocyanate dispersion with a poly(active hydrogen) compound in the presence of a polyurethane reaction catalyst wherein said polymer/polyisocyante dispersion comprises a polymer in a polyisocyanate, wherein said polymer is a reaction product of an ethylenically unsaturated macromolecular monomer, a functional monomer, and at least one other ethylenically unsaturated monomer.
 21. The polyurethane elastomer, adhesive, sealant, or coating of claim 20 wherein said poly(active hydrogen) compound is a polyol, a polymer/polyol, or a mixture thereof.
 22. The polyurethane elastomer, adhesive, sealant, or coating of claim 20 wherein said other ethylenically unsaturated monomer is selected from the group consisting of vinylidene chloride, acrylonitrile, and mixtures of acrylonitrile and methyl methacrylate.
 23. The polyurethane elastomer, adhesive, sealant, or coating of claim 20 wherein said macromolecular monomer is represented by the empirical formula:

    A--X

wherein A is an oligomer soluble in said polyisocyanate and X is an ethylenically unsaturated group.
 24. The polyurethane elastomer, adhesive, sealant, or coating of claim 20 wherein said polymer contains between about 0.25 and about 20 weight percent of said ethylenically unsaturated macromolecular monomer based upon the eeight of said ethylenically unsaturated macromolecular monomer, said functional monomer, and said other ethylenically unsaturated monomer in said polymer. 